The following is the type and use of electrodes, in addition to more detailed notes and technical parameters, because the content is too much, I'm not one by one on top. If you need to do so I can send EMAIL to you.

CMC-Emagic7 HRC 52 ~ 55 3.2 * 350mm
CMC-Emagic7 can be directly welded to a cast iron and cast magical welding electrodes, welding adhesion good, starting from layer 1 to have high hardness, if you pay attention, interpass temperature, it will not rise with the increase of welding reduce the hardness; In addition, the direct welded steel Cr12MoV after heat treatment, the performance of higher hardness, specific alkaline coating can reduce the pore generation; can be welding, vertical welding, fillet welding, melting of a high fill rate can be accelerated welding efficiency, fire resistance welding at the slightly lower exchange.

CMC-E58 HRC 57 ~ 59 2.4, 3.2, 4.0
Wear resistance, hardness, high stability. Suitable for cold damage to the surfacing of steel, especially for cold forging die, rolling die, die cutter, automotive stamping die, metal stamping die cutting angle, side. For the production of cutting tools, the same can be surfacing in the low-alloy or steel in general as a cutting edge. Can also be used in production of wear parts of the hard surface.

CMC-ECI55 HRC 55-58 3.2 * 350mm
Especially suitable for deep drawing mold repair and high R-Angle Drawing hardness parts production. Welding directly on the cast iron mold GGG70L, FCD, GM241, etc ... Melting fine, with very high hardness and wear-resistant, easy to polish. An efficient welding rods (molten filling rate of 120%) ductile iron and gray cast iron and flame quenching can also be directly surfacing.

CMC-E46N HRC 45-48 2.4, 3.2
Directly in the cast iron welding, metal stamping die for wear is very effective. The first layer of weld metal austenite; from 2 layer martensite start and good wear. Flame hardening cast iron can also be directly surfacing.

CMC-E46H HRC 44-49 3.2 * 350mm
Especially suitable for R-Mo angle of chromium cast iron mold drawing parts repair and production. Melting fine, easily polished sheet metal parts to prevent scratching; high hardness, suitable for demanding drawbead manufacturing. Ductile iron and gray cast iron and flame quenching can also be directly surfacing.

CMC-E45 HRC 48 ~ 52 2.6, 3.2, 4.0
Is better for the bonding among the hardness of a steel electrode for air-cooled steel, cast steel: If ICD5, 7CrSiMnMoV ... and so on. Automobile sheet metal panels and large metal sheet metal die stamping die of the drawing, stretching repair parts can also be used for hard surface production.

CMC-E64N 3.2 * 350mm
Cast Iron welding rod, high strength, good plasticity. For gray iron and ductile iron can be machined.

CMC-ENCD HRC 25 ~ 28 3.2 * 350mm
Directly in the cast iron welding, especially for cast iron and ductile iron MoCr of welding. Iron base for a low hardness of cast iron welding rod, weld can be processed, and because the composition is very close with the cast iron, cast iron welding rod so I do not have general problems of chromatic aberration, and may be accompanied by post-weld heat treatment of cast iron. Good weldability, without pores, cracks.

CMC-E62N 3.2 * 350mm
Especially suitable for cast iron molds, due to lower nickel content, it can reduce the cost of making steel die hard surface rendering buffer layer.

CMC-E12HA HRC 55-58 2.4, 3.2, 4.0
Excellent red stripe, widely used in forging, Die, anti-wear hardfacing production, hardness, high stability, the use of the forging die, stamping die, die extension, the entire side cut mode, Cars, hot rolling wheel, production of wear parts of the hard surface.

CMC-E60A HRC 60 ~ 62 2.6, 3.2
Hardness, high stability, high temperature wear resistance. Applicable to carbon steel, low alloy steel, hard surface making the tool wear of the mechanical repair, Cars, hot forging die cold forging welding incision.

CMC-E30N high tension, high toughness of 2.6, 3.2
The bonding of high hardness steel, steel seat fixed, hard surface cast mold making backing buffer layer, cracking of the welding.

CMC-E61N 3.2 * 350mm
Suitable for all kinds of cast iron, alloy cast iron, steel and cast iron joint, nickel and its alloys, die casting or welding of water.

CMC-E7W HRC 53 ~ 55 3.2, 4.0
For air-cooled steel (ICD5) or cast steel of the knife-edge production and damage to the surfacing, especially for the production of automotive sheet metal cutting edge, piercing and flanging parts, light sheet metal stamping die cutting angle, side. For the production of cutting tools, the same as the cutting edges by welding. Can also be used in production of wear parts of the hard surface.

CMC-E47N HRC 44 ~ 50 3.2 * 350mm
Directly on the welding of cast iron electrode, used in cast iron mold of the knife-edge, extending the pressure part is very convenient.

CMC-EH10 HRC 46 ~ 52 3.2, 4.0
Applicable to the production of large forging die repair and surface reconstruction. Due to lower chromium content, and increased molybdenum, tungsten, vanadium alloy, the formation of high temperature wear and a good balance of toughness, a substantial increase in cross-sectional area of the larger hot die life. Widely used in the large hot forging die, forging die, hot gravity die casting, production of wear parts of the hard surface.

CMC-EH13 HRC 55 ~ 58 2.4, 3.2
Thermal processing tools for damage resistance welding, in particular, are eager to tools, hot cutting tools, hot corner cutting edge of planing tools. Processing tools for the production of the cut, the same can be welding or in low-alloy steel as a general cutting edge.

Here are some commonly used electrode types, for your reference:

CMC-Emagic7 HRC 52 ~ 55 3.2 * 350mm
CMC-Emagic7 can be directly welded to a cast iron and cast magical welding electrodes, welding adhesion good, starting from layer 1 to have high hardness, if you pay attention, interpass temperature, it will not rise with the increase of welding reduce the hardness; In addition, the direct welded steel Cr12MoV after heat treatment, the performance of higher hardness, specific alkaline coating can reduce the pore generation; can be welding, vertical welding, fillet welding, melting of a high fill rate can be accelerated welding efficiency, fire resistance welding at the slightly lower exchange.

CMC-E58 HRC 57 ~ 59 2.4, 3.2, 4.0
Wear resistance, hardness, high stability. Suitable for cold damage to the surfacing of steel, especially for cold forging die, rolling die, die cutter, automotive stamping die, metal stamping die cutting angle, side. For the production of cutting tools, the same can be surfacing in the low-alloy or steel in general as a cutting edge. Can also be used in production of wear parts of the hard surface.

CMC-ECI55 HRC 55-58 3.2 * 350mm
Especially suitable for deep drawing mold repair and high R-Angle Drawing hardness parts production. Welding directly on the cast iron mold GGG70L, FCD, GM241, etc ... Melting fine, with very high hardness and wear-resistant, easy to polish. An efficient electrode (molten filling rate of 120%) ductile iron and gray cast iron and flame quenching can also be directly surfacing.

CMC-E46N HRC 45-48 2.4, 3.2
Directly in the cast iron welding, metal stamping die for wear is very effective. The first layer of weld metal austenite; from 2 layer martensite start and good wear. Flame hardening cast iron can also be directly surfacing.

CMC-E46H HRC 44-49 3.2 * 350mm
Especially suitable for R-Mo angle of chromium cast iron mold drawing parts repair and production. Melting fine, easily polished sheet metal parts to prevent scratching; high hardness, suitable for demanding drawbead manufacturing. Ductile iron and gray cast iron and flame quenching can also be directly surfacing.

CMC-E45 HRC 48 ~ 52 2.6, 3.2, 4.0
Is better for the bonding among the hardness of a steel electrode for air-cooled steel, cast steel: If ICD5, 7CrSiMnMoV ... and so on. Automobile sheet metal panels and large metal sheet metal die stamping die of the drawing, stretching repair parts can also be used for hard surface production.

CMC-E64N 3.2 * 350mm
Cast Iron welding rod, high strength, good plasticity. For gray iron and ductile iron can be machined.

CMC-ENCD HRC 25 ~ 28 3.2 * 350mm
Directly in the cast iron welding, especially for cast iron and ductile iron MoCr of welding. Iron base for a low hardness of cast iron welding rod, weld can be processed, and because the composition is very close with the cast iron, cast iron welding rod so I do not have general problems of chromatic aberration, and may be accompanied by post-weld heat treatment of cast iron. Good weldability, without pores, cracks.

CMC-E62N 3.2 * 350mm
Especially suitable for cast iron molds, due to lower nickel content, it can reduce the cost of making steel die hard surface rendering buffer layer.

CMC-E12HA HRC 55-58 2.4, 3.2, 4.0
Excellent red stripe, widely used in forging, Die, anti-wear hardfacing production, hardness, high stability, the use of the forging die, stamping die, die extension, the entire side cut mode, Cars, hot rolling wheel, production of wear parts of the hard surface.

CMC-E60A HRC 60 ~ 62 2.6, 3.2
Hardness, high stability, high temperature wear resistance. Applicable to carbon steel, low alloy steel, hard surface making the tool wear of the mechanical repair, Cars, hot forging die cold forging welding incision.

CMC-E30N high tension, high toughness of 2.6, 3.2
The bonding of high hardness steel, steel seat fixed, hard surface cast mold making backing buffer layer, cracking of the welding.

CMC-E61N 3.2 * 350mm
Suitable for all kinds of cast iron, alloy cast iron, steel and cast iron joint, nickel and its alloys, die casting or welding of water.

CMC-E7W HRC 53 ~ 55 3.2, 4.0
For air-cooled steel (ICD5) or cast steel of the knife-edge production and damage to the surfacing, especially for the production of automotive sheet metal cutting edge, piercing and flanging parts, light sheet metal stamping die cutting angle, side. For the production of cutting tools, the same as the cutting edges by welding. Can also be applied to wear parts of the hard surface production.

CMC-E47N HRC 44 ~ 50 3.2 * 350mm
Directly on the welding of cast iron electrode, used in cast iron mold of the knife-edge, extending the pressure part is very convenient.

CMC-EH10 HRC 46 ~ 52 3.2, 4.0
Applicable to the production of large forging die repair and surface reconstruction. Due to lower chromium content, and increased molybdenum, tungsten, vanadium alloy, the formation of high temperature wear and a good balance of toughness, a substantial increase in cross-sectional area of the larger hot die life. Widely used in the large hot forging die, forging die, hot gravity die casting, production of wear parts of the hard surface.

CMC-EH13 HRC 55 ~ 58 2.4, 3.2
Thermal processing tools for damage resistance welding, in particular, are eager to tools, hot cutting tools, hot corner cutting edge of planing tools. Processing tools for the production of the cut, the same can be welding or in low-alloy steel as a general cutting edge.